Grade |
C (Max) |
Mn (Max) |
P (Max) |
S (Max) |
Si (Max) |
Cr |
Ni |
Mo |
Nitrogen (Max) |
Cu/ Others |
301 |
0.15 |
2.00 |
0.045 |
0.030 |
1.00 |
16.00 – 18.00 |
6.00 – 8.00 |
- |
0.10 |
- |
304 |
0.08 |
2.00 |
0.045 |
0.030 |
0.75 |
18.00 – 20.00 |
8.00- 10.50 |
- |
0.10 |
- |
304L |
0.030 |
2.00 |
0.045 |
0.030 |
0.75 |
18.00 – 20.00 |
8.00- 12.00 |
- |
0.10 |
- |
310S |
0.08 |
2.00 |
0.045 |
0.030 |
1.50 |
24.00- 26.00 |
19.00 – 22.00 |
- |
- |
- |
316 |
0.08 |
2.00 |
0.045 |
0.030 |
0.75 |
16.00 – 18.00 |
10.00 – 14.00 |
2.00 – 3.00 |
0.10 |
- |
316L |
0.030 |
2.00 |
0.045 |
0.030 |
0.75 |
16.00 – 18.00 |
10.00 – 14.00 |
2.00 – 3.00 |
0.10 |
- |
317 |
0.08 |
2.00 |
0.045 |
0.030 |
0.75 |
18.00 – 20.00 |
11.00 – 14.00 |
3.00 – 4.00 |
0.10 |
- |
317L |
0.030 |
2.00 |
0.045 |
0.030 |
0.75 |
18.00 – 20.00 |
11.00 – 15.00 |
3.00 – 4.00 |
0.10 |
- |
321 |
0.08 |
2.00 |
0.045 |
0.030 |
0.75 |
17.00 – 19.00 |
9.00 – 12.00 |
- |
0.10 |
Ti5 ( C + N ) Min or 0.70 max |
347 |
0.08 |
2.00 |
0.045 |
0.030 |
0.75 |
17.00 – 19.00 |
9.00 – 13.00 |
- |
- |
Cb= 10x ( C Min ) or 1.00 Max |
409 |
0.08 |
1.00 |
0.040 |
0.010 |
1.00 |
10.50 – 11.75 |
0.50 |
- |
- |
Ti= 6x (C+ N ) Min or 0.70 Max |
409M |
0.03 |
0.81.2 |
0.030 |
0.030 |
0.40.75 |
11.00- 12.00 |
1.5 max. |
- |
- |
Ti= 6x (C) Min or 0.70 Max |
410S |
0.08 |
1.00 |
0.040 |
0.030 |
1.00 |
11.50- 13.50 |
0.60 |
- |
- |
- |
410 |
0.15 |
1.00 |
0.040 |
0.030 |
1.00 |
11.50- 13.50 |
0.75 |
- |
- |
- |
420 |
0.35 |
0.50 |
0.035 |
0.015 |
0.50 |
12.00 – 13.00 |
0.20.3 |
- |
- |
- |
430 |
0.12 |
1.00 |
0.040 |
0.030 |
1.00 |
16.00 – 18.00 |
0.75 |
- |
- |
- |
JSL AUS |
0.08 |
7.08.0 |
0.070 |
0.030 |
0.75 |
15.50 – 16.50 |
4.25 – 4.75 |
- |
- |
0.9 – 1.10 |
JS- 203 |
0.08 |
9.2510.25 |
0.070 |
0.030 |
0.75 |
14.25 – 15.25 |
2.25 – 2.75 |
- |
- |
1.60- 2.0 |
301M |
0.10 |
4.55.5 |
0.060 |
0.030 |
0.75 |
14.50 – 15.50 |
6.0 – 7.0 |
- |
- |
1.70- 1.90 |
* Thickness of 1.27mm & below will have elongation of 20% min. |
Chemical Composition,% |
Tensile Test |
|||||||
Designation |
C max. |
Si |
P max |
S max |
Tensile Strength Kgf/mm2 |
Yield Point Kgf/mm2,min. |
Elongation |
|
Test Piece |
%, min |
|||||||
IS 2002-1 |
0.18 |
.010-0.35 |
0.40 |
0.40 |
37-45 |
55 |
5.65/So 4/So |
26 30 |
IS 2002-2A |
0.20 |
0.10-0.35 |
0.050 |
0.050 |
42-50 |
50 |
5.65/So 4/So |
25 29 |
IS 2002-2b |
0.22 |
0.10-0.35 |
0.050 |
0.050 |
52-62 |
50 |
5.65/So 4/So |
20 24 |
Chemical Composition,% |
Tensile Test |
Bend test |
|||
Designation |
C Si Mn P S Max Max Max |
Yield Point Tensile Strength Kgf/mm2 Kgf/mm2.(N/mm2) |
Elongation %, Test Piece |
Angle of Bend |
Inside Radius |
AG |
0.09 tr.0.20-0.40 0.30 0.030 |
– – |
– – |
Chemical Composition,% |
Tensile Test*1 | 1. (i) Refer to (1) for ASTM A 203 (ii) Refer to (2) for ASTM A 203 (iii) Refer to (4) for ASTM A 203. |
|||||||
Designation |
C max |
Mn max |
P max |
S max |
Tensile Strength ksi (MPa), |
Yeild Strengh ksi(MPa),min. |
Elongation,% min |
||
GL=8 in. GL=2 in |
|||||||||
A 285 A |
0.17 |
0.90 |
0.035 |
0.040 |
45-65 (310-450) |
24(165) |
27 30 |
||
A 285 B |
0.22 |
0.90 |
0.035 |
0.040 |
50-70(385-485) |
27(185) |
25 28 |
||
A 285 C |
0.28 |
0.90 |
0.035 |
0.040 |
55-75(380-515) |
30(205) |
23 27 |
Grade |
Tensile Strength Mpa, (Min) |
Yield Strength Mpa, (Min) |
%Age Elongation in 50mm gauge length min |
Hardness (Max) |
|
BHN |
Rb |
||||
301 |
515 |
205 |
40 |
217 |
95 |
304 |
515 |
205 |
40 |
201 |
92 |
304L |
485 |
170 |
40 |
201 |
92 |
310S |
515 |
205 |
40 |
217 |
95 |
316 |
515 |
205 |
40 |
217 |
95 |
316L |
485 |
170 |
40 |
217 |
95 |
317 |
515 |
205 |
35 |
217 |
95 |
317L |
515 |
205 |
40 |
217 |
95 |
321 |
515 |
205 |
40 |
217 |
95 |
347 |
515 |
205 |
40 |
201 |
92 |
409 |
380 |
170 |
20 |
179 |
88 |
409M |
430 |
275 |
20 |
187 |
90 |
410S |
415 |
205 |
22 |
183 |
89 |
410 |
450 |
205 |
20 |
217 |
89 |
420 |
700( max ) |
- |
15 |
217 |
95 |
430 |
450 |
205 |
22 |
183 |
89 |
JSL AUS |
515 |
205 |
40 |
217 |
95 |
JS- 203 |
515 |
205 |
40 |
217 |
95 |
301M |
515 |
205 |
40 |
217 |
95 |
Chemical Composition,% |
Tensile Test |
|||||||
Designation |
C max. |
Si |
P max |
S max |
Tensile Strength Kgf/mm2 |
Yield Point Kgf/mm2,min. |
Elongation |
|
Test Piece |
%, min |
|||||||
IS 2002-1 |
0.18 |
.010-0.35 |
0.40 |
0.40 |
37-45 |
55 |
5.65/So 4/So |
26 30 |
IS 2002-2A |
0.20 |
0.10-0.35 |
0.050 |
0.050 |
42-50 |
50 |
5.65/So 4/So |
25 29 |
IS 2002-2b |
0.22 |
0.10-0.35 |
0.050 |
0.050 |
52-62 |
50 |
5.65/So 4/So |
20 24 |
Nominal Broe |
Outside Diameter |
Schedule 5S |
Schedule 10S |
Schedule 40S |
Schedule 80S |
Schedule 160S |
Schedule XXS |
|||||||
mm |
INCH |
mm |
Wt mm |
Weight (Kg/mt) |
Wt mm |
Weight (Kg/mt) |
Wt mm |
Weight (Kg/mt) |
Wt mm |
Weight (Kg/mt) |
Wt mm |
Weight (Kg/mt) |
Wt mm |
Weight (Kg/mt) |
3 |
1/8 |
10.3 |
1.24 |
0.276 |
1.24 |
028 |
1.73 |
0.37 |
2.41 |
0.47 |
- |
- |
- |
- |
6 |
1/4 |
13.7 |
1.24 |
0.390 |
1.65 |
049 |
2.24 |
0.631 |
3.02 |
.0.80 |
- |
- |
- |
- |
10 |
3/8 |
17.1 |
1.24 |
0.490 |
1.65 |
0.63 |
2.31 |
0.845 |
3.20 |
1.10 |
- |
- |
- |
- |
15 |
1/2 |
21.3 |
1.65 |
0.800 |
2.11 |
1.00 |
2.77 |
1.27 |
3.75 |
1.62 |
4.75 |
1.94 |
7.47 |
2.55 |
20 |
3/4 |
26.7 |
1.65 |
1.03 |
2.11 |
1.28 |
2.87 |
1.68 |
3.91 |
2.20 |
5.54 |
2.89 |
7.82 |
3.63 |
25 |
1 |
33.4 |
1.65 |
1.30 |
2.77 |
2.09 |
3.38 |
2.50 |
4.55 |
3.20 |
6.35 |
4.24 |
9.09 |
5.45 |
32 |
1.1/4 |
42.2 |
1.65 |
1.65 |
2.77 |
2.70 |
3.56 |
3.38 |
4.85 |
4.47 |
6.35 |
5.61 |
9.70 |
7.77 |
40 |
1.1/2 |
48.3 |
1.65 |
1.91 |
2.77 |
3.11 |
3.68 |
4.05 |
5.08 |
5.41 |
7.14 |
7.25 |
10.16 |
9.54 |
50 |
2 |
60.3 |
1.65 |
2.40 |
2.77 |
3.93 |
3.91 |
5.44 |
5.54 |
7.48 |
8.74 |
11.1 |
11.07 |
13.44 |
65 |
2.1/2 |
73.0 |
2.11 |
3.69 |
3.05 |
5.26 |
5.16 |
8.63 |
7.01 |
11.4 |
9.53 |
14.9 |
14.2 |
20.39 |
80 |
3 |
88.9 |
2.11 |
4.51 |
3.05 |
6.45 |
5.49 |
11.30 |
7.62 |
15.2 |
11.1 |
21.3 |
15.24 |
27.65 |
100 |
4 |
114.3 |
2.11 |
5.84 |
3.05 |
8.36 |
6.02 |
16.07 |
8.56 |
22.3 |
13.49 |
33.54 |
17.12 |
41.03 |
125 |
5 |
141.3 |
2.77 |
9.47 |
3.40 |
11.57 |
6.55 |
21.8 |
9.53 |
31.97 |
15.88 |
49.11 |
19.05 |
57.43 |
150 |
6 |
168.3 |
2.77 |
11.32 |
3.40 |
13.84 |
7.11 |
28.3 |
10.97 |
42.7 |
18.2 |
67.56 |
21.95 |
79.22 |
200 |
8 |
219.1 |
2.77 |
14.79 |
3.76 |
19.96 |
8.18 |
42.6 |
12.7 |
64.6 |
23.0 |
111.2 |
22.23 |
107.8 |
250 |
10 |
273.1 |
3.40 |
22.63 |
4.19 |
27.78 |
9.27 |
60.5 |
12.7 |
96.0 |
28.6 |
172.4 |
25.40 |
155.15 |
300 |
12 |
323.9 |
3.96 |
31.25 |
4.57 |
36.00 |
9.52 |
73.88 |
12.7 |
132.0 |
33.32 |
238.76 |
25.40 |
186.97 |
350 |
14 |
355.6 |
3.96 |
34.36 |
4.78 |
41.3 |
11.13 |
94.59 |
19.05 |
158.08 |
35.71 |
281.70 |
- |
- |
400 |
16 |
406.4 |
4.19 |
41.56 |
4.78 |
47.29 |
12.7 |
123.30 |
21.41 |
203.33 |
40.46 |
365.11 |
- |
- |
450 |
18 |
457.2 |
4.19 |
46.80 |
4.78 |
53.42 |
14.27 |
155.80 |
23.8 |
254.36 |
45.71 |
466.40 |
- |
- |
500 |
20 |
508.0 |
4.78 |
59.25 |
5.54 |
68.71 |
15.09 |
183.42 |
26.19 |
311.2 |
49.99 |
564.68 |
- |
- |
600 |
24 |
609.6 |
5.54 |
82.47 |
6.35 |
94.45 |
17.48 |
255.41 |
30.96 |
442.08 |
59.54 |
808.22 |
- |
- |
STANDARD |
WERKSTOFF NR. |
UNS |
JIS |
BS |
GOST |
AFNOR |
EN |
SS 304 |
1.4301 |
S30400 |
SUS 304 |
304S31 |
08Х18Н10 |
Z7CN18‐09 |
X5CrNi18-10 |
SS 304L |
1.4306 / 1.4307 |
S30403 |
SUS 304L |
3304S11 |
03Х18Н11 |
Z3CN18‐10 |
X2CrNi18-9 / X2CrNi19-11 |
SS 304H |
1.4301 |
S30409 |
- |
- |
- |
- |
- |
SS 304H |
1.4301 |
S30409 |
- |
- |
- |
- |
- |
SS 310 |
1.4841 |
S31000 |
SUS310 |
310S24 |
20Ch25N20S2 |
- |
X15CrNi25-20 |
SS 310S |
1.4845 |
S31008 |
SUS310S |
310S16 |
20Ch23N18 |
- |
X8CrNi25-21 |
SS 310H |
- |
S31009 |
- |
- |
- |
- |
- |
SS 316 |
1.4401 / 1.4436 |
S31600 |
SUS 316 |
316S31 / 316S33 |
- |
Z7CND17‐11‐02 |
X5CrNiMo17-12-2 / X3CrNiMo17-13-3 |
SS 316L |
1.4404 / 1.4435 |
S31603 |
SUS 316L |
316S11 / 316S13 |
03Ch17N14M3 / 03Ch17N14M2 |
Z3CND17‐11‐02 / Z3CND18‐14‐03 |
X2CrNiMo17-12-2 / X2CrNiMo18-14-3 |
SS 316H |
1.4401 |
S31609 |
- |
_ |
_ |
_ |
_ |
SS 316Ti |
1.4571 |
S31635 |
SUS 316Ti |
320S31 |
08Ch17N13M2T |
Z6CNDT17‐123 |
X6CrNiMoTi17-12-2 |
SS 317 |
1.4449 |
S31700 |
SUS 317 |
320S31 |
- |
- |
- |
SS 317L |
1.4448 |
S31703 |
SUS 317L |
320S31 |
- |
- |
X2CrNiMo18-15-4 |
SS 321 |
1.4541 |
S32100 |
SUS 321 |
320S31 |
- |
- |
X6CrNiTi18-10 |
SS 321 |
1.4541 |
S32100 |
SUS 321 |
320S31 |
- |
- |
X6CrNiTi18-10 |
SS 321H |
1.4878 |
S32109 |
SUS 321H |
320S31 |
- |
- |
X12CrNiTi18-9 |
SS 347 |
1.4550 |
S34700 |
SUS 347 |
- |
08Ch18N12B |
- |
X6CrNiNb18-10 |
SS 347H |
1.4961 |
S34709 |
SUS 347H |
- |
- |
- |
X6CrNiNb18-12 |
STANDARD |
WERKSTOFF NR. |
UNS |
JIS |
BS |
KSI |
AFNOR |
EN |
SS 904L |
1.4539 |
N08904 |
SUS 904L |
904S13 |
STS 317J5L |
Z2 NCDU 25-20 |
X1NiCrMoCu25-20-5 |